Under high-vacuum condition at residual gases pressure less than 10?7 Pa, the structure of both chromium films deposited on the bare glass surface and glass surface predeposited with ultra-thin germanium underlayers are investigated. As shown, by means of the germanium sublayers within the 0–4 nm thickness range, it is possible to control crystallites’ linear sizes and change the degree of substrate-surface filling with atoms of chromium in the film layers in the range of mass thickness of 1–2 nm.