«Микроволновое спекание биокерамики на основе наноструктурного биогенного гидроксиапатита»
791–796 (2013)

PACS numbers: 61.43.Gt, 62.23.St, 68.37.Hk, 81.05.Rm, 81.20.Ev, 87.15.La, 87.85.jj

A given paper is concerned with both study of the possibility of fabrication of porous ceramics by microwave sintering at 1100?C for medical application based on biogenic hydroxyapatite and investigation of properties of prepared materials, according to the maintain at the maximum temperature. As revealed, increasing of maintain time at the maximum sintering temperature from 5 to 30 minutes leads to reducing of porosity from 37 to 33% and retains open porosity more than 95%, and, correspondingly, increases the compressive strength from 38 to 59 MPa.